520. Grune, E.; Johann, T.; Appold, M.; Wahlen, Ch.; Blankenburg, J.; Leibig, D.; Müller, A.H.E.; Gallei, M.; Frey, H.: One-Step Block Copolymer Synthesis versus Sequential Monomer Addition: A Fundamental Study Reveals that one Methyl Group Makes a Difference, Macromolecules 51, 3527 (2018) -- DOI: 10.1021/acs.macromol.8b00404
Abstract:
Block copolymers of polyisoprene and polystyrene are key materials for polymer nanostructures as well as for several commercially established thermoplastic elastomers. In a combined experimental and kinetic Monte Carlo simulation study, the direct (i.e., statistical) living anionic copolymerization of a mixture of isoprene (I) and 4-methylstyrene (4MS) in nonpolar media was investigated on a fundamental level. In situ1H NMR spectroscopy enabled to directly monitor gradient formation during the copolymerization and to determine the nature of the gradient. In addition, a precise comparison with the established copolymerization of isoprene and styrene (I/S) was possible. Statistical copolymerization in both systems leads to tapered block copolymers due to an extremely slow crossover from isoprene to the styrenic monomer. For the system I/4MS the determination of the reactivity ratios shows highly disparate values with rI = 25.4 and r4MS = 0.007, resulting in a steep gradient of the comonomer composition. The rate constants determined from online NMR studies were used for a kinetic Monte Carlo simulation, revealing structural details, such as the distribution of the homopolymer sequences for both blocks, which are a consequence of the peculiar kinetics of the diene/styrene systems. DFT calculations were used to compare the established copolymerization of isoprene and styrene with the isoprene/4-methylstyrene system. A variety of gradient copolymers differing in molecular weight and monomer feed composition were synthesized, confirming strong microphase segregation as a consequence of the blocklike structure. The one-pot synthesis of such tapered block copolymers, avoiding high vacuum or break-seal techniques, is a key advantage for the preparation of ultrahigh molecular weight block copolymers (Mn > 1.2 × 106 g/mol) in one synthetic step. These materials show microphase-segregated bulk structures like diblock copolymers prepared by sequential block copolymer synthesis. Because of the living nature of the tapered block copolymer structures, a vast variety of complex structures are accessible by the addition of further monomers or monomer mixtures in subsequent steps.

There are additional file downloads belonging to this publication

Password

powered by php + PostgreSQL - last modified 2021-08-27- Impressum